98% Content of Steel Grinding Tool Silicon Carbide

Basic Info

Model No.: 98%SiC

Refractoriness (℃): 1770< Refractoriness< 2000

Feature: Long Time Materials

Type: Refractory Material

Shape: Block

Material: Silicon Carbide

SiC: 98%

Fe2O3: 0.02%max

F.C: <0.2%

AL2O3: 0.05%max

CaO: 0.05%max

MgO: 0.05%max

H2O: 0.5%max

Additional Info

Packaging: Woven bag, lined with plastic film bags, each 25kg can also be packaged according to customer demand.

Productivity: 10000tons/month

Brand: Yi Feng Rui Da

Transportation: Ocean,Land

Place of Origin: SHIZUISHAN CHINA

Supply Ability: 100000tons

Certificate: IS9001

Port: TIAN JIN CHINA

Product Description

1.Product Introduction

Add silicon metal powder and carbon in silicon carbide (graphite, carbon black, etc.) at 1450 ℃ is buried carbon burning, silicon powder and the carbon reaction type low temperature beta SiC, combine the original silicon carbide particles.Because the products generally contain free silicon 8% ~ 15% and small amounts of free carbon, so use temperature below 1400 ℃.Its thermal conductivity and impact resistance are good, but the strength, hardness and corrosion resistance are poor.Reaction sintered silicon carbide products are almost invariable before and after sintering, so they can be processed into any shape and size, especially for large scale and complex shapes

2.Product Application

Silicon carbide used for 3-12 inch monocrystalline silicon, polycrystalline silicon, potassium arsenide, quartz crystal wire cutting. Solar photovoltaic industry, semiconductor industry, piezoelectric crystal industry, engineering materials.Silicon carbide for semiconductor, lightning rod, circuit components, high temperature applications, UV detectors, structural materials, astronomy, disc brakes, clutch, diesel particulate filter, filament pyrometer, ceramic film, cutting tools, heating elements , Nuclear fuel, jewelry, steel, protective gear, catalyst support and other fields.

3.Product Index

4.Product process

⑴, broken raw materials

Hammer crusher for petroleum coke crushing, crushing to the process requirements of the particle size.

⑵, ingredients and mixing

Ingredients and ingredients are in accordance with the provisions of the formula weighing and mixing process. The project ingredients using platform, mixing concrete mixer, according to process requirements of petroleum coke and quartz sand ingredients, mixing operations.

⑶, silicon carbide furnace preparation:

Furnace preparation is the last furnace used to re-trim, finishing, to put into use again. Operations include cleaning the bottom of the furnace material, trimming the electrode, cleaning furnace wall and repair, to load capacity, 1 block, inspection, troubleshooting other furnace defects.

⑷, loading furnace

Loading furnace is in accordance with the provisions of the charge type, location, size of the furnace filled with reaction materials, insulation materials, furnace core material, and masonry with the role of insulation and Sheng Smelting furnace side walls.

⑸, power smelting silicon carbide:

Smelting furnace and transformer connected to the power. Power transmission 15min vote to open fire, light CO, smelting process lasted 170h.

⑹, cooling

After the silicon carbide smelting furnace is shut down, it is naturally cooled, and then the griddle (unloading furnace wall, scumbard material) continues to be naturally cooled.

⑺, baked grading

Silicon carbide furnace classification is removed from the furnace crystal block, graphite, and the first grade, two products, graphite and other things separated from the process. Silicon carbide baked furnace grading using furnace classification, artificial cleavage of the crystal tube, the bulk of the barrel into the graded field, the classification of artificial.

5.Packing And Transportion

Woven bag, lined with plastic film bags, each 25kg can also be packaged according to customer demand.

Transportation and handling: During the transportation process, the silicon carbide shall not be dragged with hook, should prevent mixing with hard materials. It should belight unloading to reduce packaging crushing.

Storage: The silicon carbide should be stored in a cool and dry place, to prevent rupture of bags, to prevent moisture and other substances to affect the product. Storage  should away from sources of pollution.